Question? Just ask us!
Free Encyclopedia of Building & Environmental Inspection, Testing, Diagnosis, Repair
InspectAPedia ® Home
ROOFING INSPECTION & REPAIR
AMERICAN CEMWOOD ROOFING
BEST ROOFING PRACTICES
BUILT UP ROOFS
CATHEDRAL CEILING VENTILATION
CERTIFICATIONS for ROOFING CONTRACTORS
CHIMNEY FLASHING Mistakes & Leaks
COLD WEATHER ROOF TROUBLE
DECKS, ROOFTOP CONSTRUCTION
EPDM, RUBBER, PVC ROOFING
EXTRACTIVE BLEEDING on SHINGLES
FIRE RETARDANT PLYWOOD
FLASHING on BUILDINGS
FLAT ROOF MOISTURE & CONDENSATION
Green House or Solarium Roof Leaks
HEAT TAPES & CABLES on Roofs for Ice Dams
ROOF ICE DAM LEAKS
MASONITE WOODRUF FIBERBOARD ROOFING
NOISE CONTROL for ROOFS
PLASTIC ROOFING TYPES
PVC, EPDM, RUBBER ROOFING
ROOF ARCHITECTURAL STYLES - PHOTO GUIDE
ROOF CLEANING RECOMMENDATIONS
ROOF COLOR RECOMMENDATIONS
ROOF INSPECTION SAFETY & LIMITS
ROOF LEAK DIAGNOSIS & REPAIR
ROOF NOISE TRANSMISSION
ROOF REPLACEMENT SNAFUs
ROOFING FELT UNDERLAYMENT REQUIREMENTS
ROOFING MATERIALS, Age, Types
SADDLE CONSTRUCTION at CHIMNEYS
SNOW GUARDS & SNOW BRAKES
STANDARDS for ROOFING
STRESS SKIN INSULATED PANELS
TEST LABS - ROOF SHINGLE
TREES & SHRUBS, TRIM OFF BUILDING
TRUSSES, Floor & Roof
UNDERLAYMENT REQUIREMENTS on ROOFS
VENTILATION in BUILDINGS
WALK-ON ROOF SURFACES
WARRANTIES for ROOF SHINGLES
WORKMANSHIP & ROOF DAMAGE
Slate roof inspection, diagnosis & repair guide: this series of detailed slate roof inspection and repair articles describes procedures for evaluating the condition of slate roofing. How to inspect, identify defects, and estimate remaining life of slate roofs are addressed. This slate roofing article series also references slate repair procedures, repair slate sources, slate tool sources, and slate quarries around the world.
Green links show where you are. © Copyright 2014 InspectApedia.com, All Rights Reserved.
Our photo (left) shows a slate roof being replaced in Duluth Minnesota.
[Click to enlarge any image]
Like many building topics, opinions run heavier than actual data. The abandonment of good slate roofs which should have been repaired is a financial shame and the destruction of a valued asset.
same time, careless optimism about a bad slate roof which is at the
end of its life risks an angry inspection client. This article reviews
types of slate, common defects, inspection topics, and some repair
tips. We also provide slate sources and where to buy slate roofing materials and slate roofing tools and products.
Watch out: before walking on a slate roof, see ROOF INSPECTION SAFETY & LIMITS
A Very Short History of Slate Roofs & The Composition of Slate
According to the US NPS "Roofing for Historic buildings" article series:
An abbreviated original version of this article appeared in the winter 1991 issue of the ASHI Technical Journal - the content has been extensively edited with corrections to the original, additional in-depth text explaining items cited in the original article and adding new material, as well as adding about hundreds of color photographs of slate types and slate roofs for this online version. Copies of the ASHI Technical Journal are available from the American Society of Home Inspectors - ASHI at ashi.com.
Green link shows where you are in this article series.
Frequently Asked Questions (FAQs) about how to inspect slate roofs
Questions & answers or comments about slate roof troubleshooting, leak diagnosis, & repair .
Use the "Click to Show or Hide FAQs" link just above to see recently-posted questions, comments, replies, try the search box just below, or if you prefer, post a question or comment in the Comments box below and we will respond promptly.
Search the InspectApedia website
HTML Comment Box is loading comments...
Technical Reviewers & References
Related Topics, found near the top of this page suggest articles closely related to this one.
See SLATE ROOF INSPECTION PROCEDURE for details of this topic.
Alan Carson & Dan Friedman
Every slate roof looks terrific when it's wet - unless you're seeing leaks inside. There are, fortunately, some better ways to look at and think about this material. Slate roof failures result from breakdown of the material itself, from poor installation, or from poor maintenance.
Evaluation of the condition of slate roofing, and estimating its remaining life considers at least these factors:
This article discusses these concerns. Other very important factors in evaluating the condition of a building roof such as the condition of roof decking or sheathing, and roof structure and framing, and condition of valleys and other flashings. Many of the slate roof defects discussed below are illustrated in our online Slate Roof Photo Library included below in this document.
Inspectors should be cautious in evaluating roof condition to avoid failing the roof material itself when leaks are confined to flashing areas. We've found good Vermont slate roofs which have been "roofed over" with asphalt (and ruined) when the leaks were located in and only in metal valleys. Metal flashings may be deteriorating from slate particles washing off of the roof.
We read repair suggestions in the Old-House Journal involving use of roofing cement and felt for temporary purposes, as well as the preferable soldered or replacement repairs. We've found severe corrosion, particularly on copper, when asphalt roof cement has been used for temporary repairs. In our opinion this is a poor short-term repair which causes increased damage. On an historic restoration project involving slate roofs with copper flashings the worst corrosion we found on the copper was where roof cement had been used to patch leaks. Other patches and materials over similar leaks caused much less apparent damage.> are not considered in this discussion but must indeed be evaluated by the inspector.
See Types of Roofing Slate for details of this topic.
Variations occur in color, thickness, surface texture, graduated sizes and varying widths. Standard slate roofs use slates 3/16" to 1/4" thick of one uniform length and width with square tails laid to a line in a conventional shingling pattern.
Textural style roofs use rough-textured slates with uneven butts and varied thickness. Different colors and varying sizes are often used. The resulting roof has a very rustic look.
Graduated slate roofs use slates which vary in size and often in thickness, with larger slates at the eaves, smaller and with less shingle exposure at the ridge. Original work graduated roofs show smooth transition among the sizes from larger to smaller as each course of slates approaches the ridge line. Where lots of repair work was done this effect may have been lost. This roof style makes the roof and building look larger and taller than it actually is.
Shingle exposure is the portion of the shingle which you can see from outside, or the portion left exposed to the weather. In most shingle roofing systems the exposed portion of the shingle is considerably less than the total shingle length.
In addition to color, graduated and textural patterns, slates are placed in a variety of shingling patterns, of which several are illustrated in sketches throughout this paper and in the Slate Roof Photo Library, such as French, Dutch-lap, and open-lap patterns. The Dutch lap uses a 3" side overlap and a vertical exposure of all but 3" of the slate. The result is essentially a single layer of roofing with only 3" of overlap at the top and side. The open joints are all on one side or the other along any given row or course of slates. This system is extra vulnerable to wind-driven rain.
The French method slate pattern also offers essentially a single layer of roofing with three inches around the perimeter of each shingle.
Finally, slates have a natural "grain" in the material. Normally the slates are cut so that the grain runs the length of the slates. If the slate is quarried improperly, the nail holes create a perforated effect on the slate and it will break in half at the nail holes after the installation. Watch for this interesting defect.
See this slate edge close up, showing the natural layering of mineral deposits in the original stone.
See Slate Colors, Chemistry for details of this topic.
According to the National Slate Association slate is a stone material which has an indefinite life.
Slate Roofs, reprinted by the Vermont Structural Slate Co. We caution readers that while this is absolutely the best reference we've found on slate roofing, the language on durability is a bit enthusiastic. You'll have to look closely at the footnotes to identify the less durable materials.
Because the actual composition of slate affects its durability (and cost), the identification of the source of existing slates is useful in evaluating the condition and future life of a roof. Common sources of roofing slates used in the US and Canada are Pennsylvania, Virginia, and Vermont. California, Georgia, Michigan, New York and Maine also have or had slate quarries. In 1924 the remaining active slate quarrying areas were Maine, Vermont-New York, Pennsylvania, and Virginia. Common slate names have British origins. Maine's Bangor recalls Bangor blue mined in North Wales.
Identification of the slate source by visual inspection is difficult by other than experienced slate handlers or laboratories. However as the slate source has such a dramatic effect on the expected life of the material, any anecdotal, historical, or visual clues are useful. Readers are cautioned not to assume that slates in their area necessarily came only from the nearest slate quarry. Though that's a reasonable bet in many cases, one might find Virginia slate or Maine slate on roofs as distant from the quarries as British Columbia! Vermont Structural Slate Co. will identify slates if you mail them a 1.5"x1.5" triangular sample.
Basic slate roofing colors, their composition, and their sources
Basic roofing slate colors are black, blue-black, gray, blue-gray, purple, mottled purple and green, green, and red. These color names should be preceded by designations of "unfading" or "weathering" (discussed later). Color is determined by variations in chemical and mineral composition.
The mineral composition of the shale from which slates are cut varies significantly among quarries and from state to state in the US. The primary constituents are white and black mica.
See later details in this article. A detailed procedure for analysis of slates was documented in US Geological Survey Bulletin #700, "The Analysis of Silicate and Carbonate Rocks", by Dr. W.F. Hillebrand.
Virginia roofing slate colors & characteristics
Virginia Roofing Slate is blue-gray in color, tough, durable, and considered a top quality material by most slate sources. This slate is notable for a peculiar luster giving attractive lights and shadows on roofs.
Vermont roofing slate colors & characteristics
Vermont roofing slate is typically green with purple, black, and red available. Vermont green slate is the most abundant, with well developed cleavage (easy to split into roofing slates), with good "fissibility" (relatively easy to work), making it the most common variety used. Slate from Vermont is lower in lime content than the Pennsylvania variety. Chemical composition of slates varies of course by quarry as does slate color. Slates are available in both fading and non-fading varieties. In Vermont slate fading color is not considered an indication of deterioration. Rather it's an aesthetic factor.
Blue-gray Pennsylvania roofing slate colors & characteristics
Pennsylvania blue-gray slate is possibly the best known and most widely distributed of the common slate colors. Some architects and roofers call these slates Pennsylvania black. But as "Black-Bed" slates, a less durable material, might be confused with the better quality Pennsylvania material, the blue-gray name should be used.
Unfading Pennsylvania gray roofing slate color, appearance, characteristics
This is probably a Pennsylvania Gray slate roof on a NY College Campus in Poughkeepsie. Unfading Pennsylvania gray slate, which weathers or fades less than "weathering" varieties, has soft gray tones and may have additional strength or durability. Unfading Pennsylvania black, heavier than other slates, has a rougher appearance and does not, as its name claims, fade significantly. [Fading may be taken to mean a general "lightening" across the slate.] Blue-black "hard-vein" Pennsylvania slates are hard material which grows darker on exposure to weather.
Gray and Grey-Black roofing slates, where they are from, and their characteristics
Gray and gray-black roofing slates are quarried in Vermont and parts of New York. The gray is lighter than the Pennsylvania blue-gray. You may find it mixed with purple. Gray-black is quarried in both light and dark grays, some with a mottled effect. Unfading green, weathering green, unfading purple, unfading mottled purple and green, variegated purple have been quarried in Vermont and New York.
Unfading red roofing slate, where it is quarried, and its wear characteristics
Ribbon Slates, why they were used, and their wear characteristics
Most references claimed that ribbon slates were inferior and likely to have a shorter life due to their mineral inclusions. However in New York one of the authors (DF) has observed ribbon slate roofs which appeared to be in good condition after 90 years.
These slates were selected for cosmetic beauty in some installations and for lower price in others. The inspector needs to examine the specific roof to determine if the ribbon slates involved are deteriorating from mineral wash-out or alternatively if they are in good condition.
Freak slate colors, what are "freak roofing slates"?
If you find slate which is not one of these colors it's a "freak". It would be rare to find a freak which was quarried thinner than 1/4", usually in greater thickness up to 2". Some are not true slates in every quality and may not be salvageable when worn or on roofs in poor condition.
See Slate Roof Aging and Durability for details of this topic.
Close-up Inspection of Slate Roofs is Necessary to Evaluate Their Condition
We were warned by an experienced slate roofer and we have confirmed by field inspections of slate roofs that determination of slate condition other than by direct up-close inspection is highly unreliable. Slates may look fine from the ground, but be found soft and at end of life on close inspection. By direct inspection we mean looking at slates from a few inches, either from a ladder or some other point of view such as an attic window. We strongly advise inspectors not to walk on slate roofs. Risks include falling - very slippery, and extensive damage to the slates.
Trapasso, personal communication.
The photographs provided here show how soft roofing slates can become. These slates might, from a distance, look pretty good, but I was easily able to crush the slates with my fingers. we do not agree that we should call this "rotted roofing slate" as did Trapasso, but on seeing how soft and delaminated this slate can become, we can understand his loose use of that term.
Roofing Slate Life Depends on From Where Slates were Quarried
Life expectancy of Virginia Buckingham roofing slate
Darker gray "Buckingham" slates from Virginia are considered a durable high-quality material which, properly maintained, can have a near indefinite life. Average life of these slates is 175 years.
The Old House Journal, April, 1983 p. 57
Life expectancy of Vermont roofing slate
Vermont slate roofs, with proper maintenance, can last indefinitely.
The Old House Journal, April 1983, p.58, and Slate Roofs, National Slate Association, p. 71.
By other sources, Vermont slates have life expectancy of 100-200 years.
Steven Trapasso, personal communication. Also the Old House Journal April 1983 rates Vermont slates as having a 175 year life.
Such roofs should be maintained, not replaced. With proper maintenance such an asset may be continued for an indefinite period. Inspectors who do not know the composition and source of slates would not want to condemn, except in the worst of circumstances, a Vermont slate roof.
Life expectancy of Pennsylvania roofing slate
Typical life for Pennsylvania slate roofs is 40-50 years. These life expectancies are general experience with the material and do not consider installation or environmental factors which vary from one building to the next.
Life expectancy of British and Welsh roofing slate
Earlier British experimentation on slate durability and composition emphasized that variations in the tendency of slates to absorb water
may be the principal cause of deterioration seen by modern inspectors. Slates which are soft, delaminating, and thus are at or near end of their
useful life may have been damaged by frost. "That sort of slate", said Dr. Watson, the bishop of Llandaff, "other circumstances being
the same, is esteemed the best, which imbibes the least water; for the imbibed water not only increases the weight of the covering, but,
in frosty weather, being converted into ice, it swells and shivers the slate."
Watson continued to suggest that slates, being less porous than clay roofing tiles of the day, were more durable. --The New Practical Builder and Workman's Companion
Watson's opinion that slates are more durable than clay tiles is arguable as both materials are found with considerable variation in composition. Indeed unglazed clay absorbs more water (up to 10%) than slate (usually 1%) but tiles are not necessarily damaged by these freeze-thaw conditions. Watson's comments pertain to use of slate in Britain.
The extent of color change in Pennsylvania [and possibly other] slates often indicates the extent of deterioration. More white, more efflorescence probably means more deteriorated.
What is the normal rate of deterioration of roofing slates?
The rate of slate deterioration on roofs depends on the source quarry and the depth from which the slates were cut. These determine the density and composition of the slate. Site conditions, such as the roof pitch, exposure to sun, building moisture and ventilation and exposure to mechanical damage also affect slate life. It is interesting to note that several references indicate that slates actually harden after being quarried and exposed. We'd presume that observation pertains to the early or initial state of use of the slates, and we found no reference which claimed some chemical or molecular process of permanent or continuing hardening over life.
Signs of deteriorating roofing slate
Deteriorating Pennsylvania slate shows a mottled appearance, with white faded patches resulting from exposure to sunlight and moisture. The white areas generally begin at the three exposed sides of a slate, growing towards the center of the slate as a function of time and exposure.
The white visible in Pennsylvania slate is evidence of efflorescence - lime deposited on the slate surface. If the whole slate is white in color and scaling you should consider the slate to be at the end of its life. However as long as the slates are physically intact the roof is serviceable. If a roofer recommends tearing off the whole roof you should ask to be shown examples of failed slates.
Roofing slate fading versus mottling
Fading versus mottling: It is important for an inspector to distinguish between the mottled edges-in whitening (efflorescence) and fading. By contrast to the efflorescence process, fading slates generally fade monotonically across the slate rather than from edges in. Faded slates will not show an obvious whitish powder of surface deposited mineral salts as thick as that left by efflorescence. All slates will fade from weather exposure. Those which have only minimal color change are classed as "permanent" or "unfading". Those which change more markedly are classed as "weathering".
Monotonically means that the color change is even across the material rather than showing up as a splotch, or a ring of white around darker color, or in other variations. It's a nice word, not recommended for inspection reports.
We've heard several explanations for the mechanism by which Pennsylvania slates deteriorate, of which the most interesting was the opinion that lime in the slates in the presence of moisture reacts to break down organic components in the slate. For slates higher in carbon or carbonaceous materials this may be indeed the most accurate explanation. Pennsylvania "Black Bed" quarried slates were high in carbonaceous impurities and were recommended by the Slate Association only for temporary buildings or for chalkboards. By the 1920's this slate was recognized as not as durable; you'd not expect to find it surviving on a building in 1991.
The National Slate Association reference does not detail the mechanism of slate deterioration. It does point out that the slate roof on the Saxon Chapel at Stratford-on-Avon was built 1100 years ago - still in good condition.
Does slate "rot"? By Mr. Trapasso's account the decomposition of Pennsylvania slate may be understood as a process similar to decomposition of wood. The lime which was in the slate, when the slate was mined, had not caused deterioration because the slates were protected from sunlight. When the slate is split, cut, punched for use, the lime is in an inactive or dormant state.
Following application on a roof surface the slate material is exposed to ultraviolet rays (sunlight) and moisture. These components cause the lime to break down the organic materials in the slate (shale), making the slate increasingly porous and causing the white efflorescence. Lime and other mineral salts are dissolved and deposited on the surface of the slate when moisture evaporates.
Slate Roofs, National Slate Association, p.71-76.
Calcium Oxide - Sources of white minerals and oxides in roofing slates
Examining quantitative analysis of slates from nineteen quarries we observe that while oxides of silica (SIO2) and aluminum oxide (AL2O3) are the dominant components of slates, almost all have measurable levels of calcium oxide (CaO) and other carbonates and oxides. There are dramatically higher levels of these materials in Pennsylvania slates (3%) than in slates from Vermont (.3%-.7%). Clearly there is more material available to form calcium carbonates and efflorescence in the shorter lived materials. -- Slate Roofs p. 73 Carbon, which would be broken down in the process described by Trapasso, occurs in slates from only a few quarries, and then in usually small amounts of less than 1%. This would seem to argue against the "slate rots" explanation of deterioration.
Brown staining in roofing slate
The known chronological age of slates may be available from an owner or other documentation. As with all materials, experienced inspectors rate the apparent wear age of the roof, not the actual age.
Snow Guards on Slate Roofs
This snow guard intended to keep snow from sliding off of the roof, avoiding gutter damage or avoiding falling snow at building entrances.
See Ribbon Slates for details of this topic
the ribbon slate on this
mansard roof slope may have been chosen for appearance, though it was not installed so as to use the ribbon diagonals to form any particular pattern.
In the first two photos at left the slates have diagonal
colored stripes of mineral inclusion, but they do not show the characteristic delamination and wear we see
on classic ribbon slates - we will replace this photo with one of the more typical ribbon slates
when we can dig some out of my library.
Some ribbon slates have proven to be quite durable while others show mineral inclusions (making the ribbons of color in the slate) that are softer than the surrounding slate material. These latter ribbon slates were often considered, and proved to be, a less durable roofing slate.
So look closely at your ribbon slates to see if the mineral colored stripes have washed out or deteriorated to form holes or soft spots. If these conditions are not present your ribbon slates may be quite durable.
See Slate Roof Installation Quality for details of this topic.
The following may all be indications that the roof is failing from the condition of the slate nails:
In our opinion, galvanized flashings (or too-thin thin copper or painted steel) are a mistake on slate roofs. The flashing is very likely to wear, rust, and fail before the slates. While replacing flashings is quite possible and appropriate, it's often expensive and if not done by an experienced slate roofer, there is risk of costly damage to the roof. We had a client this year whose slate roof was damaged by the mason working on the chimney. He accepted a low-bidder for roof repairs. We found asphalt shingles nailed over and around the area of damaged slates. To say that the roof leaked was the least aggravating observation concerning this work.
Inspecting from the attic interior may also give clues to fastener age, type, and condition if some nails are visible. You may see tips of nails, depending on the length of fasteners used.
Slate nails: Proper installations use copper, stainless, or hot-dipped galvanized nails for fastening slates. Very early slate roofs were secured using wood pegs. Later ones used tie-wires in some applications. Slaters' nails have a thinner head than conventional roofing nails, avoiding damage to the covering slates. We've found many slate roofs installed with steel nails in the Northeast. We've also found lots of roofs in that area which are losing good slates from nail failures.
Slate nail holes: When a slate is punched (usually at the quarry) the hole is driven from the back of the slate, leaving a ragged pit at the front (exposed) surface of the slate so that the nail head can be countersunk flush with the top of the slate. This avoids damage to the next course of slates which overlay the nail heads and which may crack under load.
Hand punching of nail holes in slates: Because most roofs have at least some custom slate fitting (for example at valleys), some slates are hand-punched and may be fractured around the nail hole. Usually only two holes are punched, 1.25" to 2" from either side and about a quarter of the length of the slate down from the top. More holes and more nails may be used to hang thicker heavier slates.
Where battens or spaced roof sheathing are used the spacing of the battens will affect where the holes are punched in the slates. Slates punched too close to their centers or too low in the slate are more likely to leak when water seeps down in a fan-shaped pattern from the vertical abutment of the sides of the slates in the next course up the roof. If you are inspecting a roof which frequently leaks following prolonged rains, and if the slates and flashings look pretty good, and if leaks are everywhere, you might look for improper punching or nailing errors. Don't rush to condemn the roof - how often and how badly does it leak? Under what conditions? What is being damaged? Where is water going?
Nail tightness: Slates should hang loosely on the nail. Nails too tight may break the slate as they're pulled through it as wood shrinks. Nails not driven fully are likely to break the slate above.
Other signs of poor installation include inadequate side laps. Side Lapped slate pattern.
Side laps on slate roofs should be not less than 3" and each side-joint should be as near as possible to the center of the slate below. Particularly where improper repairs have been done you may find violations of this rule. Inadequate side laps risk leaks as a result of wind-driven rain. Inadequate side laps might be suspected on roofs which use varying-width or graduated width shingles. However some experienced roofers and inspectors commented that graduated, random-width, graduated width slate roofs were more costly than other slate systems and were often installed by more skilled roofers. Do not mistake graduated or random slate sizes for necessarily improper application.
See Other factors in Condition for details of this topic.
Roof slope, as with all roof systems, is a big factor in shingle wear. The steeper the slope, the more durable the roof. Slates have been used even on flat roofs, as ballast, and slates were used to line the reflecting pool at the US Capitol in Washington DC.
Condensation in attic interiors can be a problem. All slate roofs need ventilation to equalize the temperature between inside and outside the roof surface. Elimination of unwanted moisture in winter and heat in summer will both extend roof life. Serious damage from interior moisture is likely to be to roof sheathing and framing, but high interior moisture will shorten the life of most roof coverings as well. The open lap slate pattern was probably intended for use on buildings with high interior moisture - perhaps a cow barn.
Most normal slate roof installations, as originally built, may have had adequate ventilation. In our opinion, serious moisture problems may begin when modern renovations insulate between rafters and add interior finishes in attics. For those designs special provisions may be needed to cool and dry the roof cavity.
Mineral deposits found on the interior surface (attic view) of slates, when none are visible outside, are a sign of possible attic moisture problems. Where no outside staining or efflorescence match inside findings, the inspector may suspect that sun exposure is drying the outer surface leaving longer moist conditions inside. If these conditions are not consistent on all roof surfaces you may find the most mineral deposits on the north or shaded roof surfaces.
Moss on slates should be considered as damaging as on any other type of shingle. The moss retains moisture against the slate and its roots may actually penetrate and damage the material. On older roofs with heavy moss the growth can actually lift and separate the shingles. Chemical treatments may help with moss as it does on wood roofs. Extreme care should be used in working with chemicals.
Roof framing for slate roofs is often stronger than similar framing for houses of the same age for which lighter roof materials were used. A slate roof can weigh as little as 700 pounds per square up to 8000 pounds where 2" thick slates were used on a graduated slate roof. On a residential building the maximum weight per square you'd probably find would be 2500 pounds. The addition of slate to a house not framed for this purpose will require an analysis of the roof framing system.
one roofing square is 100 sq. ft.
Clues about the quality of a slater's work may be found in hip and ridge design. This topic is not discussed here. Flashing details, valley flashing methods, weather exposure, mechanical damage from falling limbs, foot traffic or improper workmanship, are examples of other factors which affect roof life. They are not discussed here.
See Alan Carson's "Slate Roof" presentation notes used at several ASHI Seminars.
See Slate Roof Repair history for details of this topic.
Tar or roofing mastic is normally an indication of improper maintenance. It should be considered a temporary, unreliable repair. Tar or roofing cement should not be found at chimneys, sidewall flashings, plumbing vents, or elsewhere. The tar itself usually remains effective as a sealant only for a year or so. While in place, tar traps moisture within the slates, causing the slate itself to deteriorate. When flashings leak on a roof they should be repaired or replaced as necessary, without using roof cement.
Copper tabs and fastener failures: Watch for numerous copper tabs at the center of replacement shingles. These indicate that repairs have been made and they may be a clue about the overall condition of the fasteners. In a first-class slate repair you should not be able to see the copper tabs. The Old-House Journal April 1984 roofing issue describes an alternative method for securing slates which will leave a copper tab exposed. Expert roofers have a less visible method of fastening the replacement slate. [See "Repairing Slates" sidebar article.]
Asphalt shingles applied over slate: Using asphalt over slates is surprisingly common "re-roof" procedure as it avoids labor and disposal costs for the slate material. [In some areas of the Northeast it also represents the popularity of lower-cost asphalt and the dearth of experienced slaters who might have repaired the slate roof.] When nailing the asphalt shingles it is common to find only a poor bond of new nails to original roof decking. The slates below tend to chip and bulge the new material resulting in a "peanut brittle" or "popcorn" effect. Since the comparatively large thermal mass of the slates retains heat, the asphalt shingles are "cooked" from their backside as well as from their front when exposed to sunlight. The life of such shingles is estimated by some to be half the normal span.
See Slate Roof Leaks for details of this topic.
All slate roofs probably have at least some flashing, slate, or other damage or mechanical installation errors. Some conditions such as a side lap error, damaged slate, or even flashing error may leak only in certain weather conditions such as windy rain storms from a particular direction, water backup behind ice dams, or prolonged rains. Where slates are missing near valleys the adjoining slates may be damaged as well. Openings may cause leaks or water to pass below the valley flashing even if the flashing looks intact. Where there were previous repairs it's common for the felt underlayment to be torn as well. If there are porous slates or openings above the tears in the felt, water may leak through.
Ice dams at roof eaves can be a serious leak source on slate as most other roof systems. Traditionally 30# felt was used at eaves as "insurance" against this problem. Some slate suppliers recommend this heavier felt for all underlayment, not just at the eaves. However two components conspire to reduce the effectiveness of felt as ice-dam protection: every nail at the eaves punctures the felt, and with age felts often dry and disintegrate before the slates have worn out.
Slope requirements for slate roofs In conventional roofing design slates are used on roofs with a slope of at least 4" of rise in 12" of run, that is, on 4 in 12 roofs. A 3" head lap is used, often 4" when the slope is less than 8 in 12. So a 20" long slate, with a 3" head lap, would have an exposure of 8.5". For 18" slates the exposure is 7.5", and for 16" slates, 6.5". Roofs with less head lap or more exposure may be more leak-prone.
Some slate companies advertised A slate roof that cannot leak, yet [was] inexpensive, easy to apply, beautiful..., durable as time," using a design which was soon found to be a disaster: 12" slates were placed with 9" exposure, leaving 3" for headlap and 6" which was backed only by a cap sheet of 32# felt interlaced with the slates. Roofs were also installed following this poor design, using 14" slates with 10"-11" exposure. Felt is not functional as a permanent roofing material: even where it is not exposed directly to sunlight, as the organics dry out the felt cracks, disintegrates, and leaks. We have reports that inspectors have been the subject of legal actions following their failure to identify this defect in slate roofs. See the illustrations above.
Personal communication, Doug Sheldon, Vermont Structural Slate, December 1990.
See Slate Holding actions for details of this topic.
If a client cannot afford to replace a slate roof a wiser course may be to do nothing in the short run, other than to trap small leaks in an attic, or to tar leaky areas. Although these steps are not preferred, they are often better than abandoning what may be a valuable roof of predominantly durable slates.
Tarring leaks in slate roofing systems is an ugly and desperate holding action. However if a roof may be salvaged by deferring a proper repair for a short time we'd probably tolerate this step. Advising clients that the only option is to complete a very expensive slate repair immediately is likely to result in an asphalt roof-over which may, in the long run, be a worse crime. This is clearly a matter of opinion.
Where the slates are good but fasteners are failing, some roofers may be willing to remove, salvage, and reinstall slates. Slates which are less than 1/4" thick should be discarded. The increase in labor costs for this procedure makes this "re-roofing" process expensive. Some slate companies suggest that this procedure might be selected as a continuing repair/maintenance process so that over a decade of maintenance the roof has been totally replaced. It's likely that the total labor bill for a drawn-out project will be larger than the costs of an all-at-once repair. However this approach permits spreading out a large investment over a longer and less painful period.
Personal communication, Vermont Structural Slate, December 1990
ASHI ethical guidelines require inspectors to have no financial connection with work performed on buildings they inspect. But where further evaluation and/or repair advice is needed it is perfectly proper, and in our opinion advisable, to refer clients to experienced, qualified slate roofers just as you would to an expert in another field for other concerns.
For slate roofs, refer clients only to roofers who have experience with slate materials. While we'd prefer to refer a client to three reputable experts, if we could locate only one in our area, by our opinion of what's most sensible, we'd refer to that one. Contractors who are not familiar with slate and confronted by a leak in a valley or in an area of limited mechanical damage, may sell a complete re-roofing job to an anxious owner.
Similarly, improper repairs or traffic on a roof with fragile fasteners or slates, may cause much more new damage than was present before.
This section deals with repairs to damaged slate roofs as compared with complete new slate roof installation. A key difficulty is presented by the fact that unlike asphalt shingles, slates are rigid. The repair person cannot easily "lift" adjacent slates to install the fastener for the new replacement slate.